Fracture mechanical characterization of mica-filled epoxy glass composites under monotonic and cyclic loading

Abstract

Stator insulations comprised of mica-filled epoxy glass composite materials are of paramount importance for the reliability of high-voltage rotating machines. The present work deals with the fracture mechanical characterization of the winding insulation under conditions of monotonic and cyclic loading. The identification and quantification of the weak interfaces in the material that will most likely result in the initiation and propagation of defects are investigated in detail. Material specimens are processed from insulation tapes, and tests are conducted under mode I, mode II and mixed mode (Fixed Ratio Mixed Mode) loading to characterize the weak interface. The influence of resin content on the strength of the weak interface is also investigated. The results give an indication of the delamination mechanism and a measure of the critical energy release rate in the insulation materials.

Keywords

Winding insulation mica delamination fracture mechanics cyclic loading monotonic loading critical energy release rate

Get full access to this article

View all access options for this article.

References

Brutsch

Tari

Frohlich

et al.

Insulation failure mechanisms of power generators. IEEE Electr Insul Mag 2008; 24: 17–25.

Sumereder

Weiers

. Significance of defects inside in-service aged winding insulations. IEEE Trans Energy Convers 2008; 23: 9–14.

Andraschek

Wanner

Ebner

et al.

Mica/epoxy-composites in the electrical industry: applications, composites for insulation, and investigations on failure mechanisms for prospective optimizations. Polymers 2016; 8: 201–201.

Hao Y, Jia Z, Jiang X, et al. The changes of mechanical properties of epoxy/mica insulation materials in aging process. In: Proceedings of the 6th international conference on properties and applications of dielectric materials, Xi'an, China, 21–26 June 2000, pp. 185–188. Piscataway, NJ: IEEE.

Rusu-Zagar

Notingher

Stancu

. Ageing and degradation of electrical machines insulation. J Int Sci Publ Mater Methods Technol 2014; 8: 526–546.

Stone GC, Gupta BK, Lyles JF, et al. Experience with accelerated aging tests on stator bars and coils. In: Conference record of the 1990 IEEE international symposium on electrical insulation, Toronto, Canada, 3–6 June 1990.

Lenko

Schlögl

Bichler

et al.

New approaches towards the investigation on defects and failure mechanisms of insulating composites used in high voltage applications. Compos B Eng 2014; 58: 83–90.

Braun JM, Stone GC and Seddling HG. Applications of dynamic mechanical analysis to endurance testing of generator stator bars. In: Conference record of the 1992 IEEE international symposium on electrical insulation, Baltimore, MD, 7–10 June 1992.

D3171-99:2004. Standard test methods for constituent content of composite materials.

10.

DIN EN 6033:1996. Determination of interlaminar fracture toughness energy mode I

G_{IC}

11.

ISO 15024:2001. Fibre-reinforced plastic composites, determination of mode I interlaminar fracture toughness,

G_{IC}

, of unidirectional fibre-reinforced plastic composites using a double cantilever beam (DCB) specimen.

12.

ISO 15114:2014. Fibre-reinforced plastic composites, determination of mode II fracture resistance for unidirectionally reinforced materials using the calibrated end loaded split (C-ELS) test and an effective crack length approach.

13.

Kinloch

Wang

WIlliams

et al.

The mixed-mode delamination of fibre composite materials. Compos Sci Technol 1993; 47: 225–237.

14.

Pugno

Ciavarella

Cornetti

et al.

A generalized Paris law for fatigue crack growth. J Mech Phys Solids 2006; 54: 1333–1349.

15.

D6115 97:1996. Test method for mode I fatigue delamination growth onset of unidirectional fibre-reinforced polymer matrix composites.

16.

Akatsuka

Takezawa

Kamiya

. Delamination mechanism of high-voltage coil insulators made from mica flakes and thermosetting epoxy resin. J Appl Polym Sci 2001; 79: 2164–2169.

17.

Leonesio

. An observation made on the fracture properties of mica. Eng Fract Mech 2003; 1: 237–238.

18.

Hussain

Nakahira

Nishijama

et al.

Fracture behaviour and fracture toughness of particulate filled epoxy composites. Mater Letters 1995; 27: 21–25.