Polyamide-6/organointercalated zirconium phosphate nanocomposites (PA-6/ZrPOct) were prepared by melt extrusion. The synthesized lamellar ZrP was expanded with octadecylamine at different amine:phosphate ratio, and its influence was evaluated by tensile test, melt flow rate, water absorption, rheology, scanning electron microscopy, and wide-angle X-ray diffraction. For all nanocomposites, the increase of modulus and decrease of elongation at rupture were observed. The decrease in water uptake was observed as the amine/phosphate increase, indicating that the presence of the amine reduces the hydrophilic nature of PA-6. Rheology revealed by pseudoplasticity indices that the nanofillers dispersion was homogeneous in all nanocomposites. Wide-angle X-ray diffractometry analysis showed that the characteristic basal spacing peak of pristine ZrP was absent for ZrOct 1:1 and 2:1. Also a high decrease in crystallinity was observed for PA-6/ZrOct 2:1 sample, which would be associated to plasticizing effect of octadecylamine avoiding crystallites formation. Evidences showed that structures with different degrees of intercalation and/or exfoliation could have been achieved.
BarkerJGomezR. Formation of hydrates during deepwater drilling operations. J Petrol Technol1989; 41: 297–301.
2.
HockerSHudson-SmithNSmithP, et al.Graphene oxide reduces the hydrolytic degradation in polyamide-11. Polymer2017; 126: 248–258.
3.
MazanTJørgensenJEchtermeyerA. Aging of polyamide 11. Part 2: general multiscale model of the hydrolytic degradation applied to predict the morphology evolution. J Appl Polym Sci2015; 132: 1–10.
4.
DomingosEPereiraTCastroE, et al.Monitorando a degradação da poliamida 11 (PA-11) via espectroscopia na região do infravermelho médio com transformada de fourier (FTIR). Polímeros2012; 23: 37–41.
5.
VlasveldDGroenewoldJBerseeH, et al.Moisture absorption in polyamide-6 silicate nanocomposites and its influence on the mechanical properties. Polymer2005; 46: 12567–12576.
6.
SilvaLTognanaSSalgueiroW. Study of the water absorption and its influence on the Young’s modulus in a commercial polyamide. Polym Test2013; 32: 158–164.
7.
AbachaNKubouchiMSakaiT. Diffusion behavior of water in polyamide 6 organoclay nanocomposites. Express Polym Lett2009; 3: 245–255.
8.
LiuXWuQ. Polyamide 66/Clay nanocomposites via melt intercalation. Macromol Mat Eng2002; 287: 180–180.
9.
ZulfiqarSAhmadZIshaqM, et al.Aromatic–aliphatic polyamide/montmorillonite clay nanocomposite materials: synthesis, nanostructure and properties. Mater Sci Eng A2009; 525: 30–36.
10.
AhmadZSarwarMWangS, et al.Preparation and properties of hybrid organic-inorganic composites prepared from poly(phenylene terephthalamide) and titania. Polymer1997; 38: 4523–4529.
11.
ChenT. Synthesis and characterization of novel segmented polyurethane/clay nanocomposites. Polymer2000; 41: 1345–1353.
12.
ZulfiqarSSarwarM. Mechanical and thermal behavior of clay-reinforced aramid nanocomposite materials. Scr Mater2008; 59: 436–439.
13.
WangJWangXXuC, et al.Preparation of graphene/poly(vinyl alcohol) nanocomposites with enhanced mechanical properties and water resistance. Polym Int2011; 60: 816–822.
AlbertiG. Syntheses, crystalline structure, and ion-exchange properties of insoluble acid salts of tetravalent metals and their salt forms. Acc Chem Res1978; 11: 163–170.
16.
Pérez-SantanoATrujillanoRBelverC, et al.Effect of the intercalation conditions of a montmorillonite with octadecylamine. J Colloid Interface Sci2005; 284: 239–244.
17.
WeissZValáškováMKřŸistkováM, et al.Intercalation and grafting of vermiculite with octadecylamine using low-temperature melting. Clays Clay Miner2003; 51: 555–565.
18.
MendesLSilvaDLinoA. Linear low-density polyethylene and zirconium phosphate nanocomposites: evidence from thermal, thermo-mechanical, morphological and low-field nuclear magnetic resonance techniques. J Nanosci Nanotechnol2012; 12: 8867–8873.
19.
WagenerRReisingerT. A rheological method to compare the degree of exfoliation of nanocomposites. Polymer2003; 44: 7513–7518.
20.
ChowWMohd IshakZ. Mechanical, morphological and rheological properties of polyamide 6/organo-montmorillonite nanocomposites. Express Polym Lett2007; 1: 77–83.
21.
TjongSBaoS. Preparation and nonisothermal crystallization behavior of polyamide 6/montmorillonite nanocomposites. J Polym Sci B Polym Phys2004; 42: 2878–2891.
DingYChenGSongJ, et al.Properties and morphology of supertoughened polyamide 6 hybrid composites. J Appl Polym Sci2012; 126: 194–204.
24.
KiziltasANazariBGardnerD, et al.Polyamide 6-cellulose composites: effect of cellulose composition on melt rheology and crystallization behavior. Polym Eng Sci2013; 54: 739–746.
25.
SoulestinJRashmiBBourbigotS, et al.Mechanical and optical properties of polyamide 6/clay nanocomposite cast films: influence of the degree of exfoliation. Macromol Mater Eng2011; 297: 444–454.
26.
WangMWangWLiuT, et al.Melt rheological properties of nylon 6/multi-walled carbon nanotube composites. Compos Sci Technol2008; 68: 2498–2502.
27.
Isik-GulsacIYilmazerUBayramG. Mechanical and rheological properties, and morphology of polyamide-6/organoclay/elastomer nanocomposites. J Appl Polym Sci2012; 125: 4060–4073.
28.
ChiuFLaiSChenY, et al.Investigation on the polyamide 6/organoclay nanocomposites with or without a maleated polyolefin elastomer as a toughener. Polymer2005; 46: 11600–11609.
29.
KimGMichlerGAniaF, et al.Temperature dependence of polymorphism in electrospun nanofibres of PA6 and PA6/clay nanocomposite. Polymer2007; 48: 4814–4823.
30.
LogakisEPandisCPeoglosV, et al.Structure-property relationships in polyamide 6/multi-walled carbon nanotubes nanocomposites. J Polym Sci B Polym Phys2009; 47: 764–774.