Ceramic Whisker Reinforcement of Dental Resin Composites

Abstract

Resin composites currently available are not suitable for use as large stress-bearing posterior restorations involving cusps due to their tendencies toward excessive fracture and wear. The glass fillers in composites provide only limited reinforcement because of the brittleness and low strength of glass. The aim of the present study was to reinforce dental resins with ceramic single-crystalline whiskers of elongated shapes that possess extremely high strength. A novel method was developed that consisted of fusing silicate glass particles onto the surfaces of individual whiskers for a two-fold benefit: (1) to facilitate silanization regardless of whisker composition; and (2) to enhance whisker retention in the matrix by providing rougher whisker surfaces. Silicon nitride whiskers, with an average diameter of 0.4 μm and length of 5 μm, were coated by the fusion of silica particles 0.04 μm in size to the whisker surface at temperatures ranging from 650°C to 1000°C. The coated whiskers were silanized and manually blended with resins by spatulation. Flexural, fracture toughness, and indentation tests were carried out for evaluation of the properties of the whisker-reinforced composites in comparison with conventional composites. A two-fold increase in strength and toughness was achieved in the whisker-reinforced composite, together with a substantially enhanced resistance to contact damage and microcracking. The highest flexural strength (195 ± 8 MPa) and fracture toughness (2.1 ± 0.3 MPa · m^1/2 ) occurred in a composite reinforced with a whisker-silica mixture at whisker:silica mass ratio of 2:1 fused at 800°C. To conclude, the strength, toughness, and contact damage resistance of dental resin composites can be substantially improved by reinforcement with fillers of ceramic whiskers fused with silica glass particles.

Keywords

ceramic whisker resin composite reinforcement whisker-glass fusion

Get full access to this article

View all access options for this article.

References

Altieri JV , Burstone CJ , Goldberg AJ , Patel AP (1994). Longitudinal clinical evaluation of fiber-reinforced composite fixed partial dentures: a pilot study. J Prosthet Dent 71:16-22.

American Society for Testing and Materials ( 1983). ASTM E399-83: Standard test method for plane-strain fracture toughness of metallic materials. Philadelphia, PA: ASTM.

American Society for Testing and Materials ( 1984). ASTM F417-78: Standard test method for flexural strength of electrical grade ceramics. Philadelphia, PA: ASTM.

American Society for Testing and Materials ( 1991). ASTM E384: Standard test method for microhardness of materials. Philadelphia, PA: ASTM .

Andrews P. , Riley FL (1989). The microstructure and composition of oxide films formed during high temperature oxidation of a sintered silicon nitride. J Eur Ceram Soc 5:245-256.

Antonucci JM , Stansbury JW (1990). Synthesis and properties of a polyfluorinated prepolymer multifunctional urethane methacrylate. In: Progress in biomedical polymers. Gebelein CG , Dunn RL , editors. New York: Plenum Press, pp. 121-131.

Antonucci JM , Fowler BO , Venz S. ( 1991). Filler systems based on calcium metaphosphates. Dent Mater 7:124-129.

Anusavice KJ (1996). Challenges to the development of esthetic alternatives to dental amalgam in an academic research center. Acad Dent Mater Trans 9:25-50.

ASM Composites Handbook Committee (1988). Engineering materials handbook: composites. Vol. 1. Section 2. ASM International, USA.

10.

Bayne SC , Thompson JY (1996). Mechanical property analysis of two admixed PRIMM-modified commercial dental composites. Acad Dent Mater Trans 9:238.

11.

Bayne SC , Heymann HO , Swift EJ Jr (1994). Update on dental composite restorations. J Am Dent Assoc 125:687-701.

12.

Becher P. , Wei GC (1984). Toughening behavior in SiC whisker-reinforced alumina. J Am Ceram Soc 12(C):267-269.

13.

Bowen RL , Eichmiller FC , Marjenhoff WA (1992a). Gazing into the future of esthetic restorative materials. J Am Dent Assoc 123:33-39.

14.

Bowen RL , Eichmiller FC , Marjenhoff WA (1992b). Glass-ceramic inserts anticipated for "megafilled" composite restorations. J Am Dent Assoc 122:71-75.

15.

Carberry JL , Negrych JA (1992). Orthodontic bracket and associated fabricating method. US patent 5,078,596.

16.

Christensen GJ (1996). Restoration of pediatric posterior teeth. J Am Dent Assoc 127:106-108.

17.

Corbin SB , Kohn WG ( 1994). The benefits and risks of dental amalgam. J Am Dent Assoc 125:381-388.

18.

Cross M. , Douglas WH , Fields RP (1983). The relationship between filler loading and particle size distribution in resin composite technology. J Dent Res 62:850-852.

19.

Ferracane JL (1992). Using posterior composites appropriately. J Am Dent Assoc 123:53-58.

20.

Ferracane JL , Mitchem JC (1994). Properties of posterior composites: results of round robin testing for a specification. Dent Mater 10:92-99.

21.

Ferracane JL , Mitchem JC , Condon JR , Todd R. ( 1997). Wear and marginal breakdown of composites with various degrees of cure. J Dent Res 76:1508-1516.

22.

Goldberg AJ , Burstone CJ , Hadjinikolaou I. , Jancar J. (1994). Screening of matrices and fibers for reinforced thermoplastics intended for dental applications. J Biomed Mater Res 28:167-173.

23.

Grant AA , Greener EH (1967). Whisker reinforcement of polymethyl methacrylate denture base resins. Aust Dent J 12:29.

24.

Hirata Y. , Matsushita S. , Nakagama S. , Ishihara Y. , Hori S. ( 1989). Rheological properties and consolidation of the suspension in the alumina powder-silicon nitride whisker system. J Ceram Soc Jpn 97:866-871.

25.

Hood PE , Pickers JO (1984). Silicon carbide whisker composites. US patent 4,463,058.

26.

Jordan RE , Suzuki M. (1991). Posterior composite restorations. J Am Dent Assoc 122:31-37.

27.

Krause WR , Park SH , Straup RA (1989). Mechanical properties of Bis-GMA resin short glass fiber composites. J Biomed Mater Res 23:1195-1211.

28.

Lawn BR ( 1993). Fracture of brittle solids. Ch. 8. London: Cambridge University Press.

29.

Leinfelder KF (1988). Current developments in posterior resin composites . Adv Dent Res 2:115-121.

30.

Leinfelder KF (1995). Posterior resin composites: the materials and their clinical performance. J Am Dent Assoc 126:663-676.

31.

Levenson MF (1986). The use of a clear, pliable film to form a fiberglass-reinforced splint. J Am Dent Assoc 112:79-80.

32.

Luo J. , Lannutti JJ , Seghi RR (1999). Effect of filler porosity on the abrasive resistance of nanoporous silica gel/polymer composites. Dent Mater (in press).

33.

Lutz F. ( 1996). State of the art of tooth-colored restoratives. Oper Dent 21:237-248.

34.

Mazer RB , Leinfelder KF (1992). Evaluating a microfill posterior resin composite-a five-year study. J Am Dent Assoc 123:33-38.

35.

Milewski JV (1987). Packing concepts in the use of filler and reinforcement combinations. In: Handbook of reinforcement for plastics. Milewski JV , Katz HS , editors. New York: Van Nostrand Reinhold, pp. 14-33.

36.

Robeson LM , Harris JE (1986). Silicon carbide reinforcement of poly(aryl ether ketones). US patent 4,613,645.

37.

Suzuki S. , Suzuki SH , Cox CF (1996). Evaluating the antagonistic wear of restorative materials. J Am Dent Assoc 127:74-80.

38.

Thompson JY , Bayne SC (1996). Mechanical property analysis of two admixed PRIMM-modified commercial dental glass ionomers. Acad Dent Mater Trans 9:273.

39.

Tominaga I. , Sasaki T. (1987). Iron type golf club head. US patent 4,687,205.

40.

Willems G. , Lambrechts P. , Braem M. , Celis JP , Vanherle G. (1992). A classification of dental composites according to their morphological and mechanical characteristics. Dent Mater 8 :310-319.

41.

Wilder AD Jr , Bayne SC , Heymann HO (1996). Long-term clinical performance of direct posterior composites. Acad Dent Mater Trans 9:151-169.

42.

Xu HHK (1993). Crack-bridging toughening of continuous-fiber ceramic composites at ambient and elevated temperatures (PhD thesis). University of Maryland at College Park .

43.

Xu HHK , Eichmiller FC (1997). Reinforcement of dental and other composite materials . US patent application, filed in May, 1997.

44.

Xu HHK , Ostertag CP , Braun LM , Lloyd IK (1994). Short-crack mechanical properties and failure mechanisms of Si3N4-matrix/SiC-fiber composites. J Am Ceram Soc 77:1889-1896.

45.

Xu HHK Jahanmir S. , Ives LK , Job LS , Ritchie KT (1996). Short-crack toughness and abrasive machining of silicon nitride. J Am Ceram Soc 79:3055-3064.