Manufacturing techniques and electrical properties of conductive fabrics with recycled polypropylene nonwoven selvage

Abstract

In this research, an original rotor twister machine, with a speed of 8000 rpm, spun complex ply yarns from recycled polypropylene nonwoven selvage (PPNS) and various metal wires. The core yarn was pieces of 30 g/m² recycled PPNS and the wrap yarns were 80 μm stainless steel wires. Furthermore, 80 μm stainless steel wires and 80 μm copper wires, parallel to the core yarns, reinforced the complex ply yarns. Yarns were manufactured with wrap numbers of 0.5, 1.5, 2.5, 3.5, and 4.5 turns/cm. Complex fabrics were woven with the complex ply yarns as the weft yarns and PVC-coated PET filaments as the warp yarns. These fabrics were evaluated for surface resistivity and electromagnetic shielding effectiveness (EMSE). The presence of copper reinforcement wires was found to lower the surface resistivity of the fabrics. The lowest surface resistivity was recorded for a fabric woven from yarns with a wrap number of 4.5 turns/cm; that surface resistivity was 28.7 Ω/sq. EMSE measurements showed that fabrics with varied lamination angles provided good electromagnetic shielding. The optimum EMSE measured in this research was 56.1 dB on incident frequency as 2.36 GHz, for a fabric with 0°/90°/0°/90°/0°/90° lamination angles.

Keywords

fabric formation fabrication fiber manufacture processing production yarn

Get full access to this article

View all access options for this article.

References

Steven BW Fiber Science. Englewood Cliffs NJ: Prentice Hall, 1995.

Dharmadhikary RK , Gilmore TF , Davis HA and Batra SK Thermal bonding of nonwoven fabrics. Text Prog 1995; 26: 24-32.

Lin JH , Lou CW , Lu CK and Hsing WH Processing of thermoplastic composites produced by polypropylene nonwoven selvage. J Adv Mater 2004; 36: 57-62.

Green LM , Miller AB , Agnew DA , Greenberg ML , Li J. , Villeneuve PJ and Tibshirani R. Childhood leukemia and personal monitoring of residential exposures to electric and magnetic fields in Ontario Canada. Cancer Causes Control 1999; 10: 233-243.

Green LM , Miller AB , Villeneuve PJ , Agnew DA , Greenberg ML , Li J. and Donnelly KE A case-control study of childhood leukemia in southern Ontario Canada and exposure to magnetic fields in residences. Int. J. Cancer 1999; 82: 161-170.

Habash RWY. Electromagnetics - the uncertain health risks . Potentials IEEE 2003; 22: 23-26.

Kheifets L. and Shimkhada R. Childhood leukemia and EMF: Review of the epidemiologic evidence. Bioelectromagnetics 2005; 7: 51-59.

Kheifets LI Electric and magnetic field exposure and brain cancer: a review. Bioelectromagnetics 2001; 22: 120-131.

Olden K. NIEHS report on health effects from exposure to power-line frequency electric and magnetic fields. NC 27709 National Institute of Environmental Health Sciences, 1999.

10.

Wartenberg D. Residential EMF exposure and childhood leukemia: meta-analysis and population attributable risk. Bioelectromagnetics 2001; 22: 86-104.

11.

Chen AP , Lin CM , Lin CW , Hsieh CT , Lou CW , Young YH and Lin JH Electromagnetic shielding effectiveness and manufacture technique of functional bamboo charcoal/metal composite woven. Adv Mat Res 2010; 123-125: 967-970.

12.

Chen HC , Lee KC and Lin JH Electromagnetic and electrostatic shielding properties of co-weaving-knitting fabrics reinforced composites. Compos Part A Appl Sci Manuf 2004; 35: 1249-1256.

13.

Chen HC , Lee KC , Lin JH and Koch M. Comparison of electromagnetic shielding effectiveness properties of diverse conductive textiles via various measurement techniques. J Mater Process Technol 2007; 192-193: 549-554.

14.

Cheng KB , Ramakrishna S. and Lee KC Electromagnetic shielding effectiveness of copper/glass fiber knitted fabric reinforced polypropylene composites. Compos Part A Appl Sci Manuf 2000; 31: 1039-1045.

15.

Lin JH , Chang CW , Lou CW and Hsing WH Mechanical properties of highly elastic complex yarns with spandex made by a novel rotor twister. Text Res J 2004; 74: 480-484.

16.

Lin CW and Lin JH Manufacture and application of high-performance geogrids with pp/pet composite covered yarn. Text Res J 2005; 75: 453-457.

17.

Lin JH and Lou CW Electrical properties of laminates made from a new fabric with pp/stainless steel commingled yarn. Text Res J 2003; 73: 322-326.

18.

Lou CW , Lin CM , Chen AP , Yang YC , Chen CP and Lin JH Manufacturing technique and physical property of metal wires/ pp nonwoven selvedges complex ply yarns and knitted fabrics. Adv Mat Res 2010; 97-101: 1797-1800.

19.

Chen AP , Lin CM , Hsieh CT , Yang YC , Lou CW and Lin JH Mechanical evaluation of the production of bamboo charcoal/ stainless steel complex yarns and knitted fabrics. Adv Mat Res 2010; 97-101: 1786-1789.

20.

JIS L1094. Japanese Industrial Standard; stipulating the testing methods for electrostatic propensity of woven and knitted fabrics.

21.

Yang S. , Lozano K. , Lomeli A. , Foltz HD and Jones R. Electromagnetic interference shielding effectiveness of carbon nanofiber/LCP composites. Compos Part A Appl Sci Manuf 2005 ; 36: 691-697.