MISSE 2 PEACE Polymers Atomic Oxygen Erosion Experiment on the International Space Station

Abstract

Forty-one different polymer samples, collectively called the Polymer Erosion and Contamination Experiment (PEACE) Polymers, were exposed to the low Earth orbit (LEO) environment on the exterior of the International Space Station (ISS) for nearly 4 years as part of Materials International Space Station Experiment 2 (MISSE 2). The objective of the PEACE Polymers experiment was to determine the atomic oxygen erosion yield of a wide variety of polymeric materials after long-term exposure to the space environment. The polymers range from those commonly used for spacecraft applications, such as Teflon^® FEP, to more recently developed polymers, such as high temperature polyimide PMR (polymerization of monomer reactants). Additional polymers were included to explore erosion yield dependence upon chemical composition. The MISSE PEACE Polymers experiment was flown in MISSE Passive Experiment Carrier 2 (PEC 2), tray 1, attached to the exterior of the ISS Quest Airlock. It was exposed to atomic oxygen along with solar and charged particle radiation. MISSE 2 was successfully retrieved during a space walk on July 30, 2005 during Discovery's STS-114 Return to Flight mission. Details on the specific polymers flown, flight sample fabrication, pre-flight and post-flight characterization techniques, and atomic oxygen fluence calculations are discussed along with a summary of the atomic oxygen erosion yield results. The MISSE 2 PEACE Polymers experiment is unique because it has the widest variety of polymers flown in LEO for a long duration and was exposed to an unusually clean LEO spacecraft environment. This experiment provides extremely valuable erosion yield data for spacecraft design purposes.

Keywords

Atomic oxygen erosion yield environmental degradation International Space Station space experiment low Earth orbit

Get full access to this article

View all access options for this article.

References

Banks, B.A. , Rutledge, S.K. , Auer, B.M. , and DiFilippo, F. (1990). Materials Degradation in Low Earth Orbit (LEO) , TMS Society, pp. 15-33.

Gregory, J.C. (1987). Proceedings of the NASA Workshop on Atomic Oxygen Effects, Nov. 10-11, 1986, JPL 87-14, 1987, pp. 29-30.

de Groh, K.K. , Banks, B.A. , Hammerstrom , A.M. , Youngstrom, E.E. , Kaminski, C. , Marx, L.M. , Fine, E.S. , Gummow, J.D. , and Wright, D. (2001). MISSE PEACE Polymers: An International Space Station Environmental Exposure Experiment, AIAA #2001-4923 and NASA TM-2001-211311. National Aeronautics and Space Administration, John H. Glenn Research Center at Lewis Field, Cleveland, OH.

Banks, B.A. (1997). The Use of Fluoropolymers in Space Applications , In: Modern Fluoropolymers: High Performance Polymers for Diverse Applications, John Wiley & Sons, Ltd, Chichester, UK, chapter. 4.

Anon. ( 1998). Prediction of Erosion of Polymer-Based Materials by Atomic Oxygen in LEO, Integrity Testing Laboratory Inc., Markham, Ontario, Canada. Final Report, GRC Contract #C-72917-G.

Astm. ( 1984). ASTM E 595-84 Standard Test Method for Total Mass Loss and Collected Volatile Condensable Materials from Outgassing in a Vacuum Environment , In: Annual Book of ASTM Standards. ASTM International, West Conshohocken, PA

Nasa ( 2001). MISSE Fact Sheet, http://www.msfc.nasa.gov-/NEWSROOM/background/facts/misse.html .

Pippin, G. (2006) Summary Status of MISSE-1 and MISSE-2 Experiments and Details of Estimated Environmental Exposures for MISSE-1 and MISSE-2, AFRL-ML-WP-TR-2006-4237, TECHNICAL OPERATIONS SUPPORT (TOPS) II (Delivery Order 0011), Air Force Research Laboratory, Wright-Patterson Air Force Base, OH.

Dever, J.A. Miller S.K. , Sechkar, E.A. , and Wittberg, T.N. (2006) Preliminary Analysis of Polymer Film Thermal Control and Gossamer Materials Experiments on MISSE 1 and MISSE 2, In: Proceedings of the 2006 National Space & Missile Materials Symposium in Conjunction with the 2006 MISSE Post-Retrieval Conference, June 26-30, 2006, Orlando, FL.

Supplementary Material

Please find the following supplemental material available below.

For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.

For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.

0.00 MB

0.13 MB