Al 2 O 3 -fortifed AA6061-T6 joint produced via friction stir welding: The effects of traveling speed on microstructure,mechanical,and wear properties

Abstract

In this study, 6 mm thick AA6061-T6 alloy was friction stir-welded at different traveling speeds while Al₂O₃ nano-particles were incorporated between adjoining plates. All joints were investigated macro- and micro-structurally. In addition, distribution pattern of Al₂O₃ nano-particles in the stir zone was observed via scanning electron microscopes. Although the specimen friction stir-welded at 40 mm/min exhibited the most homogeneous particles distribution, friction stir welding at 1600 rpm and 45 mm/min yielded highest tensile strength. Fractographs achieved from tensile test specimens were in close agreement with corresponding percent elongations. Surprisingly, the foregoing specimen exhibited inferior hardness to the as-received AA6061-T6 alloy. Accordingly, it was concluded that dissolution of strengthening precipitates dominated the effect of hard reinforcement particles on enhancement of hardness value. As a result of Al₂O₃ nano-particles introduction, on the other hand, wear resistance improved tremendously.

Keywords

Friction stir welding mechanical properties wear AA6061-T6

Get full access to this article

View all access options for this article.

References

Agarwal

Gokhale

Graham

et al.

Void growth in 6061-aluminum alloy under triaxial stress state. Mater Sci Eng A 2003; 341: 35–42.

Zeng

Zhang

. Effect of tool wear on microstructure, mechanical properties and acoustic emission of friction stir welded 6061 Al alloy. Acta Metall Sin English Lett 2006; 19: 9–19.

Elangovan

Balasubramanian

. Influences of tool pin profile and welding speed on the formation of friction stir processing zone in AA2219 aluminium alloy. J Mater Process Technol 2008; 200: 163–175.

Mishra

. Friction stir welding and processing. Mater Sci Eng R Rep 2005; 50: 1–78.

Gibson

Lammlein

Prater

et al.

Friction stir welding: process, automation, and control. J Manuf Process 2014; 16: 56–73.

Elangovan

Balasubramanian

. Influences of tool pin profile and tool shoulder diameter on the formation of friction stir processing zone in AA6061 aluminium alloy. Mater Des 2008; 29: 362–373.

Feng

et al.

Improving the tribological characteristics of aluminum 6061 alloy by surface compositing with sub-micro-size ceramic particles via friction stir processing. Wear 2011; 271: 1940–1945.

Barmouz

Asadi

Givi

MKB

et al.

Investigation of mechanical properties of Cu/SiC composite fabricated by FSP: effect of SiC particles’ size and volume fraction. Mater Sci Eng A 2011; 528: 1740–1749.

Faraji

Asadi

. Characterization of AZ91/alumina nanocomposite produced by FSP. Mater Sci Eng A 2011; 528: 2431–2440.

10.

Zohoor

Givi

MKB

Salami

. Effect of processing parameters on fabrication of Al–Mg/Cu composites via friction stir processing. Mater Des 2012; 39: 358–365.

11.

Shafiei-Zarghani

Kashani-Bozorg

Zarei-Hanzaki

. Microstructures and mechanical properties of Al/Al2O3 surface nano-composite layer produced by friction stir processing. Mater Sci Eng A 2009; 500: 84–91.

12.

Zhao Y, Huang X, Li Q, et al. (2015) Effect of friction stir processing with B4C particles on the microstructure and mechanical properties of 6061 aluminum alloy. Int J Adv Manuf Technol. DOI: 10.1007/s00170-014-6748-9.

13.

Standard

. E3, Standard guide for preparation of metallographic specimens, West Conshohecken, PA: ASTM Int, 2001.

14.

Standard

. E112-96. Standard test methods for determining average grain size. Annual Book of ASTM Standards, Section 3: 03.01, E112-96, Anonymous, Philadelphia, PA: American Society of Testing and Materials, 2004, pp. 313–313.

15.

Standard test methods for tensile testing of metallic materials. ASM International, 2007, Annu B ASTM Stand, 1997, p.3.

16.

Standard

. G99, Standard test method for wear testing with a pin-on-disk apparatus, Conshohocken, PA: ASTM Int West, 2006.

17.

Standard

. E384 (2010e2): standard test method for Knoop and Vickers hardness of materials, Conshohocken, PA: ASTM Stand ASTM Int West, 2010.

18.

Elangovan

Balasubramanian

. Influences of post-weld heat treatment on tensile properties of friction stir-welded AA6061 aluminum alloy joints. Mater Charac 2008; 59: 1168–1177.

19.

Handbook

ASM

. Volume 9. Metallography and microstructures 2005, pp. 12–12.

20.

Barcellona

Buffa

Fratini

et al.

On microstructural phenomena occurring in friction stir welding of aluminium alloys. J Mater Process Technol 2006; 177: 340–343.

21.

Vaidya

Koçak

Seib

et al.

Mechanical behavior of laser beam and friction stir welded aluminum alloys for airframes. Weld World-London 2004; 48: 261–274.

22.

Goodhew

. Specimen preparation in materials science, North-Holland, 1972.

23.

Dieter

Bacon

. Mechanical metallurgy 1986; vol. 3. 3rd ed. New York, NY: McGraw-Hill.

24.

Hertzberg

Vinci

Hertzberg

. Deformation and fracture mechanics of engineering materials 1996; vol. 89, New York, NY: Wiley.

25.

Shamsipur

Kashani-Bozorg

Zarei-Hanzaki

. The effects of friction-stir process parameters on the fabrication of Ti/SiC nano-composite surface layer. Surf Coatings Technol 2011; 206: 1372–1381.

26.

Dolatkhah

Golbabaei

Givi

MKB

et al.

Investigating effects of process parameters on microstructural and mechanical properties of Al5052/SiC metal matrix composite fabricated via friction stir processing. Mater Des 2012; 37: 458–464.