Restricted accessResearch articleFirst published online October, 2018
Investigating the effects of traveling speeds and post-weld heat treatment on mechanical properties of nano-Al 2 O 3 -fortified AA6061-T6 friction stir welds
In this study, 6 mm thick AA6061-T6 plates were friction stir welded (FSWed) at different traveling speeds while Al2O3 nano-particles were incorporated between adjoining plates. The solution heat treatment was applied on samples for one hour at 540 ℃ and subsequently aged for 18 h at 180 ℃ to investigate the effect of post-weld heat treatment on mechanical properties of specimens. All joints were investigated macro- and micro-structurally. The microstructural characterization of the FSWed samples was carried out using scanning electron microscopy (SEM) and light microscopy techniques. Distribution of Al2O3 nano-particles in the stir zone was studied by SEM. The specimen FSWed at 40 mm/min exhibited the most homogeneous particles distribution. Tensile properties including ultimate tensile strength, elongation, and fracture surfaces were studied. Microhardness of specimens was also investigated. Surprisingly, all specimens exhibited inferior hardness compared to the as-received AA6061-T6 alloy. This phenomenon was attributed to the dissolution of precipitates during FSW process.
MaisonnetteDSueryMNeliasDet al.Effects of heat treatments on the microstructure and mechanical properties of a 6061 aluminium alloy. Mater Sci Eng A2011; 528: 2718–2724.
6.
MalardBDe GeuserFDeschampsA. Microstructure distribution in an AA2050 T34 friction stir weld and its evolution during post-welding heat treatment. Acta Mater2015; 101: 90–100.
7.
YangWWangMZhangRet al.The diffraction patterns from β″ precipitates in 12 orientations in Al–Mg–Si alloy. Scr Mater2010; 62: 705–708.
8.
VissersRvan HuisMAJansenJet al.The crystal structure of the β′ phase in Al–Mg–Si alloys. Acta Mater2007; 55: 3815–3823.
9.
AndersenSJZandbergenHWJansenJet al.The crystal structure of the β″ phase in Al–Mg–Si alloys. Acta Mater1998; 46: 3283–3298.
10.
LiDYangXCuiLet al.Effect of welding parameters on microstructure and mechanical properties of AA6061-T6 butt welded joints by stationary shoulder friction stir welding. Mater Des2014; 64: 251–260.
11.
Shafiei-ZarghaniAKashani-BozorgSFZarei-HanzakiA. Microstructures and mechanical properties of Al/Al2O3 surface nano-composite layer produced by friction stir processing. Mater Sci Eng A2009; 500: 84–91.
12.
Shafiei-ZarghaniAKashani-BozorgSFHanzakiAZ. Wear assessment of Al/Al2O3 nano-composite surface layer produced using friction stir processing. Wear2011; 270: 403–412.
13.
BarmouzMAsadiPGiviMKBet al.Investigation of mechanical properties of Cu/SiC composite fabricated by FSP: effect of SiC particles’ size and volume fraction. Mater Sci Eng A2011; 528: 1740–1749.
14.
GomesJRRochaLACrnkovicSJet al.Friction and wear properties of functionally graded aluminum matrix composites. Mater Sci Forum2003. 423–425: 91–96.
15.
GuoJGougeonPChenX-G. Microstructure evolution and mechanical properties of dissimilar friction stir welded joints between AA1100-B4C MMC and AA6063 alloy. Mater Sci Eng A2012; 553: 149–156.
16.
MahmoudERITakahashiMShibayanagiTet al.Wear characteristics of surface-hybrid-MMCs layer fabricated on aluminum plate by friction stir processing. Wear2010; 268: 1111–1121.
17.
ChenZLiJBorbelyAet al.The effects of nanosized particles on microstructural evolution of an in-situ TiB2/6063Al composite produced by friction stir processing. Mater Des2015; 88: 999–1007.
18.
HsuCJChangCYKaoPWet al.Al–Al3Ti nanocomposites produced in situ by friction stir processing. Acta Mater2006; 54: 5241–5249.
19.
ZahmatkeshBEnayatiMHKarimzadehF. Tribological and microstructural evaluation of friction stir processed Al2024 alloy. Mater Des2010; 31: 4891–4896.
20.
CeschiniLBoromeiIMinakGet al.Microstructure, tensile and fatigue properties of AA6061/20vol.%Al2O3p friction stir welded joints. Compos Part A Appl Sci Manuf2007; 38: 1200–1210.
21.
SatoYSKokawaHEnomotoMet al.Microstructural evolution of 6063 aluminum during friction-stir welding. Metall Mater Trans A1999; 30: 2429–2437.
22.
ElangovanKBalasubramanianV. Influences of post-weld heat treatment on tensile properties of friction stir-welded AA6061 aluminum alloy joints. Mater Charact2008; 59: 1168–1177.
23.
MishraRSMaZY. Friction stir welding and processing. Mater Sci Eng R Rep2005; 50: 1–78.
24.
Bahrami M, Helmi N, Dehghani K, et al. Exploring the effects of SiC reinforcement incorporation on mechanical properties of friction stir welded 7075 aluminum alloy: Fatigue life, impact energy, tensile strength. J Material Science and Engineering A 2014; 595: 173–178.
25.
Bahrami M, Farahmand NM and Besharati GMK. Microstructural and mechanical behaviors of nano-SiC-reinforced AA7075-O FSW joints prepared through two passes. J Material Science and Engineering A 2015; 626: 220–228.
26.
HumphreysFJPrangnellPBPriestnerR. Fine-grained alloys by thermomechanical processing. Curr Opin Solid State Mater Sci2001; 5: 15–21.
27.
DolatkhahAGolbabaeiPGiviMKBet al.Investigating effects of process parameters on microstructural and mechanical properties of Al5052/SiC metal matrix composite fabricated via friction stir processing. Mater Des2012; 37: 458–464.
28.
DongPLiHSunDet al.Effects of welding speed on the microstructure and hardness in friction stir welding joints of 6005A-T6 aluminum alloy. Mater Des2013; 45: 524–531.
29.
DawoodHIMohammedKSRahmatAet al.The influence of the surface roughness on the microstructures and mechanical properties of 6061 aluminium alloy using friction stir welding. Surf Coat Technol2015; 270: 272–283.
Abdollahzadeh A, Omidvar H, Safarkhanian MA, et al. Studying microstructure and mechanical properties of SiC-incorporated AZ31 joints fabricated through FSW: the effects of rotational and traveling speeds. Int J Adv Manuf Technol. DOI 10.1007/s00170-014-6205-9.
32.
VedaniMGariboldiE. Damage and ductility of particulate and short-fibre Al–Al2O3 composites. Acta Mater1996; 44: 3077–3088.
33.
SrivatsanT. Cyclic strain resistance and fracture behaviour of Al2O3-particulate-reinforced 2014 aluminium alloy metal-matrix composites. Int J Fatigue1995; 17: 183–199.
34.
WangZGLiSSunL. Fatigue and fracture behaviors of discontinuously reinforced aluminum matrix composites. Key Eng Mater1995. 104–107: 729–748.
35.
Hamdollahzadeh A, Bahrami M, Farahmand NM, et al. Microstructure evolution and mechanical properties of nano-SiC-fortified AA7075 friction stir weldment: The role of second pass processing. J Manuf Process, dx-doi-org.web.bisu.edu.cn/10.1016/j.jmapro.2015.06.017.
36.
Farahmand NM, Parvin N and Bahrami M. Al2O3-fortifed AA6061-T6 joint produced via friction stir welding: The effects of traveling speed on microstructure, mechanical, and wear properties. J Materials Design and Applications. DOI: 10.1177/1464420715602140.
37.
Bahrami M, Besharati GMK, Dehghani K, et al. On the role of pin geometry in microstructure and mechanical properties of AA7075/SiC nano-composite fabricated by friction stir welding technique. J Materials and Design 2014; 53: 519–527.
38.
Bahrami M, Dehghani K and Besharati GMK. A novel approach to develop aluminum matrix nano-composite employing friction stir welding technique. J Materials and Design 2014; 53: 217–225.