Secondary phases,microstructures and properties of AlN ceramics sintered by adding nitrate sintering additives

AlN ceramics were sintered at a temperature range from 1650 to 1800°C through adding the Ca and Y nitrate sintering additives. Secondary phases, microstructures and properties of the AlN ceramics were studied. When the AlN ceramics are sintered at 1650 or 1675°C, CaO and Y₂O₃ from the sintering additives react with Al₂O₃ in the AlN powder to generate CaAl₄O₇ and Y₃Al₅O₁₂. Part of Y₃Al₅O₁₂ reacts with CaO and Al₂O₃ to form CaYAl₃O₇ at 1700°C. At 1800°C, CaYAl₃O₇ decomposes into CaAl₄O₇ and Y₃Al₅O₁₂. Finally, CaAl₄O₇ volatilises and only Y₃Al₅O₁₂ remains. As the sintering temperature increases, the AlN grains grow continuously and the bending strength and thermal conductivity of the AlN ceramics increase first and then decrease. The AlN ceramics sintered at 1700°C are fully dense and have the highest bending strength and thermal conductivity of 373·7 MPa and 136·7 W m⁻¹ K⁻¹ in this work.