This paper analyses various procedures for predicting crack growth as a function of the number of cycles in fretting fatigue tests with spherical contact. The evolution of the crack is calculated using fracture mechanics starting from an initial defect. Different growth laws are considered, including the behaviour of small cracks, by modifying either the threshold or the effective stress intensity factor value. Theoretical results are compared with those obtained in tests on Al 7075 T651. Results show that, although the final lives predicted by the different laws are similar, the predicted crack evolution does vary, and the most precise law is the one that modifies the growth threshold.
SumW. S.WilliamsE. J.LeenS. B.Finite element, critical-plane fatigue life prediction of simple and complex contact configurationsInt. J. Fatigue27 (2005403–416
3.
HattoriT.NakamuraM.WatanabeT.Simulation of fretting-fatigue life by using stress-singularity parameters and fracture mechanicsTribol. Int.36 (200387–97
4.
SzolwinskiM. P.FarrisT. N.Observation, analysis and prediction of fretting fatigue in 2024-T351 aluminum alloyWear221 (199824–36
5.
AraújoJ. A.NowellD.The effect of rapidly varying contact stress fields on fretting fatigueInt. J. Fatigue24 (2002763–775
6.
NavarroC.GarcíaM.DomínguezJ.A procedure for estimating the total life in fretting fatigueFatigue Frac. Engng Mater. Struct.26 (2003459–468
7.
MuñozS.NavarroC.DomínguezJ.Application of fracture mechanics to estimate fretting fatigue endurance curvesEngng Fract. Mech.74 (20072168–2186
8.
9.
NavarroC.MuñozS.DomínguezJ.Propagation in fretting fatigue from a surface defectTribol. Int.39 (20061149–1157
MuñozS.Estimación de vida a fatiga por fretting: aplicación a componentes recubiertos Doctoral Thesis, Department of Mechanical Engineering and Materials, University of Seville, Spain, 2007.
13.
FatemiA.SocieD.A critical plane approach to multiaxial fatigue damage including out-of-phase loadingFatigue Fract. Engng Mater. Struct.11 (1988145–165
14.
NavarroC.VallellanoC.DomínguezJ.Estimation of life in fretting fatigue with cylindrical contact. In Proceedings of the Seventh International Conference on Biaxial and multiaxial fatigue and fracture, Berlin, Germany, June 28–July 1, 2004, pp. 669–674 (Deutscher Verband für Material-forschung und -prüfung e.v., Berlin).
15.
NiuX.GlinkaG.Weight functions for edge and surface semi-elliptical cracks in flat plates and plates with cornersEngng Fract. Mech.36 (1990459–475
16.
El HaddadM. H.TopperT. H.SmithK. N.Prediction of non-propagating cracksEngng Fract. Mech.11 (1979573–584
17.
VallellanoC.NavarroA.DomínguezJ.Fatigue crack growth threshold conditions at notches. Part I: TheoryFatigue Fract. Engng Mater. Struct.23 (2000113–121
18.
VallellanoC.DomínguezJ.NavarroA.On the estimation of fatigue failure under fretting conditions using notch methodologiesFatigue Fract. Engng Mater. Struct.26 (2003469–478
19.
LanteigneJ.BailonJ. P.Theoretical model for FCGR near the thresholdMetall. Trans. A 12A (1981459–466
20.
Fatigue crack growth computer program, NASA/FLAGRO, L.B. Johnson Space Center, JSC-22267, 1986.
21.
WittkowskyB. U.BirchP. R.DomínguezJ.SureshS.An experimental investigation of fretting fatigue with spherical contact in 7075-T6 aluminum alloy. Fretting fatigue: current technology and practices (Eds. HoeppnerD. V.ChandrasekeranV.ElliottC. B.), ASTM STP 1367, 1999, pp. 213–227 (American Society for Testing and Materials, PA, USA).