Effects of fretting wear on rolling contact fatigue life of M50 bearing steel

Abstract

The current study presents the results and effects of fretting wear on rolling contact fatigue (RCF) life of M50 bearing steel. A fretting wear test rig was designed and developed to induce fretting scars on the surface of standard M50 rods commonly used in a three ball and rod RCF testing machine. The fretting machine was used to induce fretting scars at a Hertzian contact pressure of 1.1 GPa, in the presence of MIL-L-23699 lubricant at a frequency of 10 Hz, slip amplitude of 21 µm for different number of cycles. The fretted rods were then evaluated at a contact pressure of 1.7 and 3.4 GPa in the three ball and rod RCF tester to determine the effect of fretted scar on fatigue life. The results indicate that a fretting scar can reduce the fatigue life at 3.4 GPa by an average of 30 per cent and fretted rods operating at 1.7 GPa behave very similar to an unfretted rod operating at 3.4 GPa.

Keywords

rolling contact fatigue lubricated contact fretting wear M50 bearing steel

Get full access to this article

View all access options for this article.

References

Johansson

Numerical simulation of contact pressure evolution in fretting. J. Tribol., 1994, 116(2), 247–254.

Tallian

T. E.

Failure atlas for Hertz contact machine elements, 1999 (ASME Press, New York).

Liston

M. A.

RCF life comparison of bearing steels at two stress levels. In ASME/STLE Tribology Conference, Toronto, Canada, 1998, NTN Technical Cent, USA, Inc., Lubrication Engineering, 1999, vol. 55(6), pp. 12–19.

Kasarekar

Micro surface profiling effects on fretting wear and bending fatigue. Masters of Science Thesis, Purdue University, 2006, pp. 8–14.

Glover

A ball-rod rolling contact fatigue tester. In Rolling contact fatigue testing of bearing steels (Ed. Hoo

J. J. C.

), 1982, pp. 107–124, ASTM STP 771 (American Society for Testing and Materials).

Hui

Sadeghi

Rateick

R. G.

Frank

M. C.

Performance characteristics of jet fuel in heavily loaded contacts. Tribol. Trans., 2004, 40(2), 154–164.

Dommarco

R. C.

Bastias

P. C.

Rubin

C. A.

Hahn

G. T.

The influence of material build up around artificial defects on rolling fatigue life and failure mechanism. Wear, 2006, 260, 1317–1323.

Parry

A. A.

Waterhouse

R. B.

Wear scar contour resulting from fretting of spherical surface against a flat. Wear, 1986, 111, 237–239.

Ioannides

Bergling

Gabelli

An analytical formulation for the life of rolling bearings. Acta Polytech. Scand., 1999, 137, 58–60.

10.

Hamrock

B. J.

Schmid

S. R.

Jacobson

B. O.

Fundamentals of fluid film lubrication, 2004, pp. 48–55 and 592–614 (Marcel Dekker, Inc.).